Visit our official website for Pultrusion Products: |
|
| Glass |
- Unidirectional E-glass And ECR Boron Free Roving
- Continuous Strand Mats
- Woven Tapes
|
| Resin |
|
| Temperature Class |
- Epoxy resin based profile - class F(155°c)
- Profiles of higher temperature - Class H(200°c) can
be manufactured using special resin system on
requirement.
- Profiles with flame retardant characteristic can be
produced by adding additives to the resin system.
|
| Pultrusion Process |
- Unidirectional E-glass and Epoxy Resin System are
used for section where high Longitudinal strength is
required.
- Woven tape / CSM are used where high Bi-directional
strength are required.
- Epoxy profiles are used for high mechanical strength
and where electrical withstand values are critical
|
| Pultrusion products are:
|
Applications |
- Lasting Performance
- Light Weight & High Strength
- Corrosion Resistant
- Electro Magnetic Transparency
- Thermal Insulation
- Low temperature capabilities
- Electrical insulation
- Machinability
- Dimensional Stability
|
- Transformers
- Switchgears
- Motor Wedges
- Lightning Arrestors
- Cable Trays
|
| |
 |
size A : M 8, 10 , 12 ,
16 , 20 , 25 mm |
|
|
 |
size A : M 8, 10 , 12 ,
16 , 20 , 25 mm |
|
| |
 |
size A : L 50 × 50 × 6 mm
|
|
|
 |
size A : M 8, 10 , 12 ,
16 , 20 mm
|
|
| |
 |
| size A : |
|
10 |
17 |
19 |
25 |
25 |
34 |
40 |
|
| B : |
|
16 |
22 |
25 |
32 |
35 |
39 |
45 |
mm |
|
|
| |
 |
| size A : |
|
8 |
10 |
12 |
13 |
16 |
19 |
|
| B : |
|
6 |
8 |
10 |
10 |
10 |
12 |
mm |
|
|
| |
 |
size A : 14, 18, 24 mm
|
|
| |
 |
| size C : |
|
6 |
6.5 |
8 |
13 |
13 |
| D : |
|
6 |
6.5 |
8 |
8 |
13 |
|
|
| |
 |
| size A : 8, 10, 12, 16, 20, 22, 25,
32, 35, 45, 49, mm |
|
|
| |
| Putruded Flat Section |
| |
|
|
FLAT THK
DIM 'A' |
WIDTH DIM. 'B' |
L |
| 15 |
20 |
25 |
30 |
40 |
50 |
60 |
| 1 |
 |
|
|
 |
|
|
|
AS PER CUSTORMER REQUIREMENT |
| 2 |
|
|
|
|
|
|
|
| 3 |
|
|
|
|
|
|
|
| 6 |
|
|
|
|
|
|
|
| 8 |
|
|
|
|
|
|
|
| 10 |
|
|
|
|
|
|
|
| 12 |
|
|
|
|
|
|
|
| 16 |
|
|
|
|
|
|
|
| 20 |
|
|
|
|
|
|
|
|
|
| |